A gas-shielded, high-alloyed, flux-cored wire designed for hard-facing deposit with high hardness. Especially developed for hard-facing of parts subjected to high metal to metal wear and moderate impact. Weld metal can retain its hardness at high temperatures up to 600°C. Weld metal can be grinded and machined by diamond tools. Weld metal is resistant to cracking and must not be welded more than 3 pass. If the base metal has a high carbon content and a low weldability, a tough buffer layer with FCW 30 is recommended before hard-facing. Heat treatment after hard-facing will decrease its welded hardness.
Download or Whatsapp a PDF of this product
TAURUS MIG HRC360 is gas-shielded, high-alloyed, flux-cored wire designed for hard-facing deposit with high hardness. Especially developed for hard-facing of parts subjected to high metal to metal wear and moderate impact. Weld metal can retain its hardness at high temperatures up to 600°C. Weld metal can be grinded and machined by diamond tools. Weld metal is resistant to cracking and must not be welded more than 3 pass. If the base metal has a high carbon content and a low weldability, a tough buffer layer with FCW 30 is recommended before hard-facing. Heat treatment after hard-facing will decrease its welded hardness.
Hard-facing of hot cut-offs, shear blades, dies for pressure casting, scraper blades, conveyors, rollers, crusher rolls and worn parts in agricultural equipment.
| COMPOSITION | % |
| Carbon | 0.60 |
| Manganese | 0.20 |
| Silicon | 0.50 |
| Chromium | 5.6 |
| Molybdenum | 0.25 |
| Vanadium | 0.20 |
| Iron | Balance |
| MECHANICAL PROPERTIES | AS WELDED |
| Protection gas | CO2 |
| Wear Index | 70.2 |
| Hardness | 59 HRC |