TAURUS 70S-6 MILD STEEL MIG WIRES (SPOOL)

SKU 0.8-M Categories , ,

Produced from high quality de-oxidised rod. The products are copper coated for increased shelf life, which facilitates good electrical conductivity with reduced friction during high speed welding.

 

  • Good electrical conductivity.
  • Precision layer-wound premium quality wire.
  • Lloyds register of shipping grade DXVud, BF, 2S, 2YS, H15.

 

APPROVALS

  • Lloyds register of shipping grade DXVud, BF, 2S, 2YS, H15
  • American Bureau of shipping grade 2SA TUV

The TAURUS ER70S-6 MIG wire is produced from high quality de-oxidised rod. The products are copper coated for increased shelf life, which facilitates good electrical conductivity with reduced friction during high speed welding. The TAURUS ER70S-6 MIG wire is a premium quality wire which is precision layer-wound to produce positive, uninterrupted feeding in semi-automatic and automated systems.

 

WELDING PROCEDURE

The TAURUS ER70S-6 MIG wire is suitable for dip (short arc), spray arc and pulsed-arc transfer welding using CO2 and Argon based shielding gases.

 

WELDING POSITIONS

  • Downhand • Horizontal flat • Horizontal vertical
  • Vertical up • Overhead

 

CLASSIFICATIONS

  • AWS A5.18 ER 70s-6
  • SABS 145 Grade A
  • EN ISO 14341 G42 2 C G4Si1
  • EN ISO 636-A W 42 3 W4Si1
  • EN ISO 636-B W 49 3 W4Si1

 

APPROVALS

  • Lloyds register of shipping grade DXVud, BF, 2S, 2YS, H15
  • American Bureau of shipping grade 2SA TUV

 

AVAILABLE IN

  • 0.6mm – 5kg spool
  • 0.8mm – 5kg /15kg spool
  • 0.9mm – 1kg / 15kg spool
  • 1.0mm – 15kg spool
  • 1.2mm – 15kg spool
  • 1.6mm – 15kg spool

 

COMPOSITION VALUE
Carbon 0.07 – 0.15 %
Manganese 1.4 – 1.85 %
Silicon 0.8 – 1.15 %
Sulphur 0.035 % Max
Phosphorous 0.03 % Max
Copper Typical 0.18 %
0.4 % Max

 

MECHANICAL ( with CO₂ ) AS WELDED
0.2% Proof stress 430 MPa min
Tensile strength 510 – 570 MPa
Elongation on 50mm 26 min
Charpy V-Notch at +20°C 110 J min
Charpy V-Notch at 0°C 80 J min
Charpy V-Notch at -20°C 47 J min